Roll-to-Roll Sputtered ITO/Ag/ITO Multilayer Films for Flexible Organic Solar Cells and Flexible Heaters

Kevin Lifsey

Presented by Han-Ki Kim,1, Sung-Hyun Park, Sang-Jin-Lee and Jae Heung Lee, Department of Advanced Materials Engineering for Information and Electronics, Kyung Hee University, Korea Research Institute of Chemical Technology Chemical Materials Solutions Center

Indium tin oxide (ITO), Ag, and ITO layers were sputtered onto a flexible PET substrate with a 700 mm width by using a commercial roll-to-roll (RTR) sputtering system to use as a flexible and transparent anode for flexible organic solar cells (FOSCs) and flexible transparent heaters (FTHs) [1]. To optimize the electrical and optical properties of the ITO/Ag/ITO multilayer, the thickness of Ag layer were varied by controlling of the DC power applied on Ag targets during the RTR sputtering process. Compared to thickness control of the top and bottom ITO layer, the thickness control of the Ag layer is more effective to obtain a low sheet resistance and high transmittance ITO/Ag/ITO multilayer. At an optimized thickness of ITO (35 nm) and Ag (10 nm), a symmetric ITO/Ag/ITO multilayer showed a sheet resistance of 3.03 Ω/square and a high optical transmittance of 87.2 %. Various bending test results showed that the high failure strain of the Ag inter layer led to good flexibility of the multilayer films. Furthermore, we discuss the effect of the Ag layer thickness on the performance of FOSCs and FTHs fabricated on RTR sputtered ITO/Ag/ITO anodes.

This post is for paying members only

Subscribe

Already have an account? Log in